The chemical structure of Polypropylene means that it inherently shows high stiffness but can be brittle and not exhibit the impact performance of Polyethylene.
Our PP Grades have been designed to optimise these properties, giving moulded products both good stiffness and impact performance.
The Tensile Modulus of a polymer shows its resistance to elastic deformation under load. Polypropylene has a superior tensile modulus to polyethylenes. The combined properties of impact and stiffness result in PSDR/Salee Colour pp grades, leading the way when compared to other rotational moulding grades of polypropylene.
Heat Deflection Temperature (HDT) is the temperature at which a polymer sample deforms under a specified load. The HDT of polyethylene is lower than that of polypropylene and should not be used in high temperature environments. The HDT of our PP Grades have been tested to show that it is at the upper level for roto mouldable polypropylenes.
Polypropylene does not exhibit the low-temperature impact performance of polyethylene, but PSDR/Salee Colour pp grade have been shown to perform better than most polypropylenes commonly used in rotational moulding.
The Association of Rotational Moulders-designed Impact Test requires a machined dart to be dropped onto a rotomoulded plaque. The drop height is increased until the sample plaque breaks under the dart impact. This test is performed on test plaques which have been conditioned at room temperature, freezing point and below freezing point.
The Full Notch Creep Test (FNCT) is a widely used method to classify materials in regard to their slow-crack growth behaviours under accelerated conditions. The aim of the FNCT is to assess resistance to brittle failure. This test shows that our polypropylene grades, and in particularly RMPP141, have vastly superior resistance when in contact with surfactants. It is essential that testing is conducted with any chemical that will be in contact with the finished product at its operating temperature.
A DN63 pipe made from RMPP141 was subjected to hoop stress of 3.9 MPa at 60oC (140oF) and has exceeded 4,000 hours. This demonstrates that RMPP141 greatly exceeds the minimum pressure requirements nominated in the ISO standard for rotational moulding grades of polyethylene.
This indicates that RMPP141 can withstand higher pressures, temperatures and top loading (long term creep) than polyethylene.
Polymer materials exhibit time-dependent behaviour. When a plastic material is subjected to a constant load it deforms continuously. The material will continue to deform slowly or until rupture or yielding causes failure. All plastics creep to an extent. Polypropylene has inherently better resistance to creep than polyethylene. The creep test allows for extrapolated data which shows that, even after 20 years, RMPP141 remains superior to polyethylene after 1 year.
The (short term) Ring Stiffness is determined by measuring deflection and force applied to a section of pipe, manhole or tank. It is compressed in a radial direction at a constant rate. Polypropylene, being inherently higher in modulus than polyethylene, has higher ring stiffness. Our PSDR/Salee Colour PP grades outperform polyethylene to such an extent that, for the same ring stiffness approximately 30% less material can be used.
Testing the integrity and strength of a tank is best carried out by way of a vacuum test. This demonstrates the exceptional performance of RMPP141 and its superiority over polyethylene for tanks.
Scratch-resistance is better in a material with higher surface hardness and higher tensile strength, resulting in reduced rate of abrasion. Polypropylene is superior to polyethylene in these attributes.
PSDR/Salee Colour PP grades display higher gloss in moulded parts than polyethylene. With the difficulty in painting polyolefins, this becomes important for aesthetic applications.